With 99% magnesium chloride as raw material for high purity magnesite products due to fewer impurities difficult to produce pan-cream, back to halogen, deformation phenomena, after the brine solution with clear and transparent brine solution preparation process due to hydrolysis reaction, MgCl2 · 6H2O can brine liquid temperature was raised 80 ~ 100 ℃, until the temperature drops to 40 ℃, re-use. Dehydration of magnesium products can be shortened clotting time, especially when low temperatures more obvious advantages. Anhydrous magnesium chloride (99% magnesium chloride MgCl2) in the building materials industry magnesite use:

Blending brine solution should first add water, after adding this product to points 4-5 times gradually added 30 minutes plus one (goal is to lower the temperature brine solution) intervals. To simultaneously with stirring, so as not to spill scalding hot water, dissolve time than traditional halogen tablets appropriate extension of 2-3 hours.

Formulated with 99% magnesium chloride brine solution, because of its high purity, than traditional magnesium chloride hexahydrate was reduced more than 2-5 degrees.

As can be seen above, halogen tablets with anhydrous magnesium chloride with less than 2.3 to 2.5 times, but also reduces the production of transport, handling, storage and other expenses. Anhydrous magnesium chloride to improve product quality, while also reducing the overall cost.